Wear-resistant and fire-resistant plastic is a kind of casting material with high wear resistance and good fire resistance. It is suitable for high temperature wear-resistant parts of thermal equipment in the power, steel, glass, ceramics, building materials and other industries . · High wear resistance: It has good wear resistance and is suitable for environments with greater wear. · Good fire resistance: It has high fire resistance and is suitable for high temperature environments. · High strength: It has high mechanical strength and can withstand greater loads.
Power industry: boiler furnace, cyclone separator and other parts with severe wear;
Iron and steel industry: high temperature wear-resistant parts of heating furnaces;
Ceramic industry: used for wear-resistant parts of ceramic kilns.
Cement industry: used for wear-resistant parts of cement rotary kilns.
project | WRRC-65 | WRRC-75 | |
Al 2 O 3 ， % | 65 | 75 | |
Bulk density 110℃*24h , g/cm³ | 2.5 | 2.7 | |
Flexural strength, MPa | 110℃*24h | 6 | 7 |
1100℃*3h | 8 | 10 | |
Compressive strength, MPa | 110℃*24h | 40 | 65 |
1100℃*3h | 50 | 60 | |
Heating line change, % | 1100℃*3h | ±0.4 | ±0.4 |
Note: Technical parameters can be adjusted according to customer requirements | |||
Power industry: boiler furnace, cyclone separator and other parts with severe wear;
Iron and steel industry: high temperature wear-resistant parts of heating furnaces;
Ceramic industry: used for wear-resistant parts of ceramic kilns.
Cement industry: used for wear-resistant parts of cement rotary kilns.
project | WRRC-65 | WRRC-75 | |
Al 2 O 3 ， % | 65 | 75 | |
Bulk density 110℃*24h , g/cm³ | 2.5 | 2.7 | |
Flexural strength, MPa | 110℃*24h | 6 | 7 |
1100℃*3h | 8 | 10 | |
Compressive strength, MPa | 110℃*24h | 40 | 65 |
1100℃*3h | 50 | 60 | |
Heating line change, % | 1100℃*3h | ±0.4 | ±0.4 |
Note: Technical parameters can be adjusted according to customer requirements | |||